| Dental Alloys
/ Made in Germany Your advantages:
- Superior mechanical characteristics with
regard to precious metal alloy
- High purity, due to production is made in
continious casting process
- All physical characteristics are up to all
requirements in accordance with EN ISO 6871-1, EN ISO 6871-2,
EN 1641,
EN ISO 14971, EN 1041, EN 980, ISO/TR 14969, EN ISO 13485
|
|
|
| |
|
|
| |
METAPLUS®
VK Nickel-chrome alloy for ceramics
|
|
|
Physical
characteristics
Density: 8,2 g/cm3
Melting Range: 1'260 - 1'350 °C
Casting Temperature: 1'410 °C
Coeff. of Expansion: (20-600 °C) 14,1 µm/mK
Vickers Hardness: 210 HV 10
Tensile Strength: 580 N/mm2
Elongation: > 13 %
E-Module: 216.000 N/mm2
|
Chemical
composition in % by weight
Nickel: 61,2 %
Chrome: 25,8 %
Molybdenum: 11,0 %
Silicium: 1,5 %
Aluminium: <0,4 %
Manganese: <0,1 %
|
|
|
| |
|
| Please order a free
sample without obligation. |
|
|
| |
METAPLUS®
VP Hard Cobalt-chrome alloy for model casting |
|
Physical
characteristics
Density: 8,3 g/cm3
Melting Range: 1'335 °C
Casting Temperature: 1'390 °C
Coeff. of Expansion: (20-600 °C) 15 µm/mK
Vickers Hardness: 410 HV 10
Tensile Strength: 900 N/mm2
Elongation: > 6 %
E-Modul: 230.000 N/mm2
|
Chemical
composition in % by weight
Cobalt: 63 %
Chrome: 28,5 %
Molybdenum: 6,0 %
Silicium: 0,4 %
Wolfram: 1,0 %
Manganese: 0,6 %
Carbon: 0,5 %
- Unable laser welding able
- Model casting for parantheses
|
|
| |
|
| Please order a free
sample without obligation. |
|
|
| |
METAPLUS®
VP Soft Cobalt-chrome alloy for model casting
|
 |
Physical
characteristics
Density: 8,3 g/cm3
Melting Range: 1'385 °C
Casting Temperature: 1'440 °C
Coeff. of Expansion: (20-600 °C) 15 µm/mK
Vickers Hardness: 300 HV 10
Tensile Strength: 775 N/mm2
Elongation: > 8 %
E-Modul: 230.000 N/mm2
|
Chemical
composition in % by weight
Cobalt: 65 %
Chrome: 27 %
Molybdenum: 6,0 %
Silicium: 0,4 %
Wolfram: 1,0 %
Manganese: 0,6 %
Carbon: 0,1 %
|
| |
| |
|
| Please order a free
sample without obligation. |
|
|
| |
METAPLUS®
UNI Cobalt-chrome alloy for ceramic
|
 |
Physical
characteristics
Density: 8,4 g/cm3
Melting Range: 1'375 °C
Casting Temperature: 1'425 °C
Coeff. of Expansion: (20-600 °C) 14,5 µm/mK
Vickers Hardness: 350 HV 10
Tensile Strength: 790 N/mm2
Elongation: > 5 %
E-Modul: 230.000 N/mm2 |
Chemical
composition in % by weight
Cobalt: 63 %
Chrome: 25,5 %
Molybdenum: 1,0 %
Silicium: 1,1 %
Wolfram: 8,5 %
Manganese: 0,8 %
Carbon: <0,1 %
|
 |
| |
Please order a free
sample without obligation. |
|
| |
METAPLUS®
CC Cobalt-chrome alloy for ceramic
|
|
|
Physical
characteristics
Density: 8,3 g/cm3
Melting point: 1'320-1420° C
Coeff. of Expansion: (20-600 °C) 14,1µm/mK
Vickers Hardness: 275 HV/10
Elongation: 10%
E-Module: 190.000 MPa
|
Chemical
composition in % by weight
Cobalt: 61 %
Chrome: 28 %
Silicium: 1,65 %
Wolfram (tungsten): 8,5 %
Manganese: 0,25 %
Carbon: <0,1 %
Iron: <0,5 %
|
| |
| |
|
| Please order a
free sample without obligation. |
|